Hello there. It’s time for another update.
It’s my latest space age material. Recycling to the max, if you will.
So a month or so back I decided to see if I could melt bottles into knappable slabs in my kiln. First try, right off the bat I get it right. When you melt the bottles at cone 05 you avoid any complications with crystals forming from the kiln wash and you get a perfect melt. Because of how thin the glass slabs are, the annealing happens over night. Make sure the glass is cool to the touch before you decide to take them out into the harsh air.
Here’s the first point that I got out of the bottle glass slab.